Vanadium carbide
 |
|
| Names | |
|---|---|
| Other names
Vanadium Carbon
|
|
| Identifiers | |
| ECHA InfoCard | 100.031.917 |
|
PubChem CID
|
|
| Properties | |
| VC | |
| Molar mass | 62.953 g/mol |
| Appearance | refractory black cubic crystals |
| Density | 5.77 g/cm3 |
| Melting point | 2,810 °C (5,090 °F; 3,080 K) |
| insoluble | |
| Structure | |
| cubic, cF8 | |
| Fm3m, No. 225 | |
|
Except where otherwise noted, data are given for materials in their standard state (at 25 °C [77 °F], 100 kPa).
|
|
 (what is   ?) |
|
| Infobox references | |
Vanadium carbide is the inorganic compound with the formula VC. It is an extremely hard refractory ceramic material. With a hardness of 9-9.5 Mohs, it is possibly the hardest metal-carbide known. It is of interest because it is prevalent in vanadium metal and alloys.
Being isomorphous with vanadium monoxide, it crystallizes in the rock salt structure. Because VC and VO are miscible, samples of VC typically contain an impurity of the oxide. It is produced by heating vanadium oxides with carbon at around 1000 °C. Vanadium carbide can be formed in the (111) orientation, when formed by radio frequency magnetron sputtering. Although VC is thermodynamically stable, it converts to V2C at higher temperatures.
Vanadium carbide is used as an additive to tungsten carbide to refine the carbide crystals to improve the property of the cermet.
Vanadium Carbide has an elastic modulus of approximately 380 GPa.
...