Nanorods
In nanotechnology, nanorods are one morphology of nanoscale objects. Each of their dimensions range from 1–100 nm. They may be synthesized from metals or semiconducting materials. Standard aspect ratios (length divided by width) are 3-5. Nanorods are produced by direct chemical synthesis. A combination of ligands act as shape control agents and bond to different facets of the nanorod with different strengths. This allows different faces of the nanorod to grow at different rates, producing an elongated object.
One potential application of nanorods is in display technologies, because the reflectivity of the rods can be changed by changing their orientation with an applied electric field. Another application is for microelectromechanical systems (MEMS). Nanorods, along with other noble metal nanoparticles, also function as theragnostic agents. Nanorods absorb in the near IR, and generate heat when excited with IR light. This property has led to the use of nanorods as cancer therapeutics. Nanorods can be conjugated with tumor targeting motifs and ingested. When a patient is exposed to IR light (which passes through body tissue), nanorods selectively taken up by tumor cells are locally heated, destroying only the cancerous tissue while leaving healthy cells intact.
Nanorods based on semiconducting materials have also been investigated for application as energy harvesting and light emitting devices. In 2006, Ramanathan et al. demonstrated1 electric-field mediated tunable photoluminescence from ZnO nanorods, with potential for application as novel sources of near-ultraviolet radiation.
Zinc oxide (ZnO) nanorod, also known as nanowire, has a direct bandgap energy of 3.37 eV, which is similar to that of GaN, and it has an excitation binding energy of 60 meV. The optical bandgap of ZnO nanorod can be tuned by changing the morphology, composition, size etc. Recent years, ZnO nanorods have been intensely used to fabricate nano-scale electronic devices, including field effect transistor, ultraviolet photodetector, Schottky diode, and ultra-bright light-emitting diode (LED). Various methods have been developed to fabricate the single crystalline, wurtzite ZnO nanorods. Among those methods, growing from vapor phase is the most developed approach. In a typical growth process, ZnO vapor is condensed onto a solid substrate. ZnO vapor can be generated by three methods: thermal evaporation, chemical reduction, and Vapor-Liquid-Solid (VLS) method. In the thermal evaporation method, commercial ZnO powder is mixed with SnO2 and evaporated by heating the mixture at elevated temperature. In the chemical reduction method, zinc vapor, generated by the reduction of ZnO, is transferred to the growth zone, followed by reoxidation to ZnO. The VLS process, originally proposed in 1964, is the most commonly used process to synthesize single crystalline ZnO nanorods. In a typical process, catalytic droplets are deposited on the substrate and the gas mixtures, including Zn vapor and a mixture of CO/CO2, react at the catalyst-substrate interface, followed by nucleation and growth. Typical metal catalysts involve gold, copper, nickel, and tin. ZnO nanowires are grown epitaxially on the substrate and assemble into monolayer arrays. Metal-organic chemical vapor deposition (MOCVD) has also been recently developed. No catalyst is involved in this process and the growth temperature is at 400 ~500 °C, i.e. considerably milder conditions compared to the traditional vapor growth method. Moreover, metal oxide nanorods (ZnO, CuO, Fe2O3, V2O5, others) can be simply made by heating initial metal in air in a Thermal oxidation process. For example, to make a dense "carpet" of CuO nanorods it was found to be enough to heat Cu foil in air at 420 °C.
...
Wikipedia