Pattern welded

Pattern welding is the practice in sword and knife making of forming a blade of several metal pieces of differing composition that are forge-welded together and twisted and manipulated to form a pattern. Often called (Modern) Damascus steel, blades forged in this manner often display bands of slightly different patterning along their entire length. These bands can be highlighted for cosmetic purposes by proper polishing or acid etching. Pattern welding was an outgrowth of laminated or piled steel, a similar technique used to combine steels of different carbon contents, providing a desired mix of hardness and toughness. Although modern steelmaking processes negate the need to blend different steels, pattern welded steel is still used by custom knifemakers for the cosmetic effects it produces.

Pattern welding developed out of the necessarily complex process of making blades that were both hard and tough from the erratic and unsuitable output from early iron smelting in bloomeries. The bloomery does not generate temperatures high enough to melt iron and steel, but instead reduces the iron oxide ore into particles of pure iron, which then weld into a mass of sponge iron, consisting of lumps of impurities in a matrix of relatively pure iron, which is too soft to make a good blade. Carburizing thin iron bars or plates forms a layer of harder, high carbon steel on the surface, and early bladesmiths would forge these bars or plates together to form relatively homogeneous bars of steel. This laminating process, in which different types of steels together produces patterns that can be seen in the surface of the finished blade, forms the basis for pattern welding.

By the 2nd and 3rd century AD, the Celts commonly used pattern welding for decoration in addition to structural reasons. The technique involves folding and forging alternating layers of steel into rods, then twisting the steel to form complex patterns when forged into a blade. By the 6th and 7th centuries, pattern welding had reached a level where thin layers of patterned steel were being overlaid onto a soft iron core, making the swords far better as the iron gave them a flexible and springy core that would take any shock from sword blows to stop the blade bending or snapping. By the end of the Viking era, pattern welding fell out of use in Europe

...
Wikipedia