Magnetic-particle inspection

Magnetic particle Inspection (MPI) is a non-destructive testing (NDT) process for detecting surface and slightly subsurface discontinuities in ferromagnetic materials such as iron, nickel, cobalt, and some of their alloys. The process puts a magnetic field into the part. The piece can be magnetized by direct or indirect magnetization. Direct magnetization occurs when the electric current is passed through the test object and a magnetic field is formed in the material. Indirect magnetization occurs when no electric current is passed through the test object, but a magnetic field is applied from an outside source. The magnetic lines of force are perpendicular to the direction of the electric current, which may be either alternating current (AC) or some form of direct current (DC) (rectified AC).

The presence of a surface or subsurface discontinuity in the material allows the magnetic flux to leak, since air cannot support as much magnetic field per unit volume as metals.

To identify a leak, ferrous particles, either dry or in a wet suspension, are applied to a part. These are attracted to an area of flux leakage and form what is known as an indication, which is evaluated to determine its nature, cause, and course of action, if any.

There are several types of electrical currents used in magnetic particle inspection. For a proper current to be selected one needs to consider the part geometry, material, the type of discontinuity one is seeking, and how far the magnetic field needs to penetrate into the part.

An AC electromagnet is the preferred method for find surface breaking indication. The use of an electromagnet to find subsurface indications is difficult. An AC electromagnet is a better means to detect a subsurface indication than HWDC, DC, or permanent magnet, while some form of DC is better for subsurface defects.

After the part has been magnetized it needs to be demagnetized. This requires special equipment that works the opposite way of the magnetizing equipment. The magnetization is normally done with a high current pulse that reaches a peak current very quickly and instantaneously turns off leaving the part magnetized. To demagnetize a part, the current or magnetic field needed has to be equal to or greater than the current or magnetic field used to magnetize the part. The current or magnetic field is then slowly reduced to zero, leaving the part demagnetized.

...