Float glass process

Float glass is a sheet of glass made by floating molten glass on a bed of molten metal, typically tin, although lead and various low melting point alloys were used in the past. This method gives the sheet uniform thickness and very flat surfaces.

Modern windows are made from float glass. Most float glass is soda-lime glass, but relatively minor quantities of specialty borosilicate and flat panel display glass are also produced using the float glass process. The float glass process is also known as the Pilkington process, named after the British glass manufacturer Pilkington, which pioneered the technique (invented by Sir Alastair Pilkington) in the 1950s at their production site in St Helens, Merseyside.

Until the 16th century, window glass or flat glass was generally cut from large discs (or rondels) of crown glass. Larger sheets of glass were made by blowing large cylinders which were cut open and flattened, then cut into panes. Most window glass in the early 19th century was made using the cylinder method. The 'cylinders' were 6 to 8 feet (180 to 240 cm) long and 10 to 14 inches (25 to 36 cm) in diameter, limiting the width that panes of glass could be cut, and resulting in windows divided by transoms into rectangular panels.

The first advances in automating glass manufacturing were patented in 1848 by Henry Bessemer, an English engineer. His system produced a continuous ribbon of flat glass by forming the ribbon between rollers. This was an expensive process, as the surfaces of the glass needed polishing. If the glass could be set on a perfectly smooth, flat body, like the surface of an open pan of calm liquid, this would reduce costs considerably. Attempts were made to form flat glass on a bath of molten tin—one of the few liquids denser than glass that would be calm at the high temperatures needed to make glass—most notably in the US. Several patents were granted, but this process was unworkable at the time.

...
Wikipedia