Cold rolled steel

Cold-formed steel (CFS) is the common term for products made by rolling or pressing steel into semi-finished or finished goods at relatively low temperatures (cold working). Cold-formed steel goods are created by the working of steel billet, bar, or sheet using stamping, rolling (including roll forming), or presses to deform it into a usable product. Cold-worked steel products, such as cold-rolled steel (CRS) and sheet, are commonly used in all areas of manufacturing of durable goods, such as appliances or automobiles, but the phrase cold-formed steel is most prevalently used to describe construction materials. The use of cold-formed steel construction materials has become more and more popular since its initial introduction of codified standards in 1946. In the construction industry both structural and non-structural elements are created from thin gauges of sheet steel. These building materials encompass columns, beams, joists, studs, floor decking, built-up sections and other components. Cold-formed steel construction materials differ from other steel construction materials known as hot-rolled steel (see structural steel). The manufacturing of cold-formed steel products occurs at room temperature using rolling or pressing. The strength of elements used for design is usually governed by buckling. The construction practices are more similar to timber framing using screws to assemble stud frames.

Cold-formed steel members have been used in buildings, bridges, storage racks, grain bins, car bodies, railway coaches, highway products, transmission towers, transmission poles, drainage facilities, various types of equipment and others. These types of sections are cold-formed from steel sheet, strip, plate, or flat bar in roll forming machines, by press brake (machine press) or bending operations. The material thicknesses for such thin-walled steel members usually range from 0.0147 in. (0.373 mm) to about ¼ in. (6.35 mm). Steel plates and bars as thick as 1 in. (25.4 mm) can also be cold-formed successfully into structural shapes (AISI, 2007b).

The use of cold-formed steel members in building construction began in the 1850s in both the United States and Great Britain. In the 1920s and 1930s, acceptance of cold-formed steel as a construction material was still limited because there was no adequate design standard and limited information on material use in building codes. One of the first documented uses of cold-formed steel as a building material is the Virginia Baptist Hospital, constructed around 1925 in Lynchburg, Virginia. The walls were load bearing masonry, but the floor system was framed with double back-to-back cold-formed steel lipped channels. According to Chuck Greene, P.E of Nolen Frisa Associates, the joists were adequate to carry the initial loads and spans, based on current analysis techniques. Greene engineered a recent renovation to the structure and said that for the most part, the joists are still performing well. A site observation during this renovation confirmed that "these joists from the 'roaring twenties' are still supporting loads, over 80 years later!" In the 1940s, Lustron Homes built and sold almost 2500 steel-framed homes, with the framing, finishes, cabinets and furniture made from cold-formed steel.

...
Wikipedia