Stoneware is a rather broad term for pottery or other ceramics fired at a relatively high temperature. A modern technical definition is a vitreous or semi-vitreous ceramic made primarily from stoneware clay or non-refractory fire clay. Whether vitrified or not, it is nonporous (does not soak up liquids); it may or may not be glazed. Historically, across the world, it has usually been developed after earthenware and before porcelain, as kiln and has often been used for high-quality as well as utilitarian wares.

As a rough guide, modern earthenwares are normally fired at temperatures in the range of about 1,000°C (1,830 °F) to 1,200 °C (2,190 °F); stonewares at between about 1,100 °C (2,010 °F) to 1,300 °C (2,370 °F); and porcelains at between about 1,200 °C (2,190 °F) to 1,400 °C (2,550 °F). Historically, reaching high temperatures was a long-lasting challenge, and temperatures somewhat below these were used for a long time. Earthenware can be fired effectively as low as 600°C, achievable in primitive pit firing, but 800 °C (1,470 °F) to 1,100 °C (2,010 °F) was more typical.

Stoneware is not recognised as a category in traditional East Asian terminology, and much Asian stoneware, such as Chinese Ding ware for example, is counted as porcelain by local definitions. Terms such as "porcellaneous" or "near-porcelain" may be used in such cases. One widely recognised definition of stoneware is from the Combined Nomenclature of the European Communities, a European industry standard. It states:

Five basic categories of stoneware have been suggested:

The key raw material in stoneware is either naturally occurring stoneware clay or non-refractory fire clay. The mineral kaolinite is present but disordered, and although mica and quartz are present their particle size is very small. Stoneware clay is often accompanied by impurities such as iron or carbon, giving it a "dirty" look, and its plasticity can vary widely. Non-refractory fire clay may be another key raw material. Fire clays are generally considered refractory, because they withstand very high temperatures before melting or crumbling. Refractory fire clays have a high concentration of kaolinite, with lesser amounts of mica and quartz. Non-refractory fire clays, however, have larger amounts of mica and feldspar.

...
Wikipedia